Hastelloy C276 Sample MTC Certificate
Access a comprehensive, professionally formatted Material Test Certificate according to EN 10204-2004: 3.1 for Hastelloy C276 (ASTM F468 UNS N10276). Inspect the exact documentation your QA and engineering teams will receive with every Ananka Fasteners order.
What's Inside This Hastelloy C276 MTC Certificate
This sample mill test certificate mirrors the rigorous QA documentation package shipped with every high-performance order from Ananka Fasteners Pvt Ltd.
- Full Traceability: Certified with Lot No.: AKTR/XXX and Heat No.: HT-C27XXX.
- Chemical Composition: Detailed breakdowns including Chromium (14.62%), Molybdenum (15.54%), and Tungsten (3.426%).
- Heat Treatment Verification: Verified Solution Annealing Treatment at 1125°C followed by a Water Quench.
- Mechanical Properties: Comprehensive reporting of Tensile Strength (836.480 MPa), Yield Strength (567.320 MPa), Elongation (37.00%), Reduction Area (63.00%), and Hardness (25, 27, 28 HRC).
- Corrosion Compliance: Corrosion testing As Per ASTM G28 method 'A'.
Live Preview: Hastelloy C276 MTC Data
Review the standard parameters and layout before downloading the full document.
TC Number
S14/26-XXX
TC Date
10/04/202X
Heat Number
HT-C27XXX
Lot Number
AKTR/XXX
Bar Shape / Size
ROUND BAR / 25 mm
Material Spec
ASTM F468 UNS N10276-2026
Dimensions / Item
STUD BOLT + HEX NUT M24-3P x 120mm
Chemical Composition %
| C | Mn | P | S | Si | Cr | Ni | Mo | Co | V | W | Fe |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.015 | 0.503 | 0.022 | 0.004 | 0.034 | 14.62 | Rem | 15.54 | 1.034 | 0.090 | 3.426 | 4.83 |
| Max: 0.020 | Max: 1.000 | Max: 0.040 | Max: 0.030 | Max: 0.080 | Min: 14.500 Max: 16.500 |
- | Min: 15.00 Max: 17.00 |
Max: 2.500 | Max: 0.350 | Min: 3.000 Max: 4.500 |
Min: 4.00 Max: 7.00 |
Mechanical Properties (Test Method: ASTM A370-2024)
| TENSILE STRENGTH MPa | YIELD STRENGTH 0.2% offset MPa | % ELONGATION (L)-4D | % REDUCTION AREA | HARDNESS BHN/HRC/HRB/Hv |
|---|---|---|---|---|
| 836.480 | 567.320 | 37.00 | 63.00 | HRC: 25, 27, 28 |
| Min: 758.000 | Min: 310.000 | Min: 25.000 | - | Min: 20.00 / Max: 32.00 |
Standard References: ASTM F468 Compliance
Our MTC certificates map to the demanding industrial standards for fasteners. The test reports confirm compliance with As Per ASME/ASTM F468 UNS N10276 EDT. 2021 with respect to the tests carried out.
| Standard / Requirement | Confirmation on Certificate |
|---|---|
| Threads | Threads As per ASME B1.13M CL 6g & 6H. |
| Corrosion Test | Corrosion testing As Per ASTM G28 method 'A'. |
| Visual Inspection | 100% visual inspection carried out & found free from defects. |
| Weld Repairs | No Weld Repair Performed. |
Ananka Fasteners' Certification Details
We certify that the fastener was manufactured sampled, tested and inspected in accordance with the specification and the results have been determined to meet the requirements of the specification.
Documentation Standard
- EN 10204-2004: 3.1 Standard
- Material is free from radioactive contamination
Heat Treatments
- Solution Annealing Treatment
- Temp Recorded: 1125°C
- Quenching Medium: Water Quench
Testing Conditions
- Chemical, Mechanical & hardness test carried at room temperature 25°C
- Bright Finish Applied
Technical FAQs — Hastelloy C276 MTC Certificate
What heat treatment methodology is tracked on this certificate?
The MTC specifically logs a Solution Annealing Treatment with temperatures recorded at 1125°C, followed by a Water Quench.
What specific tests are logged on the certificate?
The MTC verifies that Chemical, Mechanical & hardness tests are carried out at room temperature 25°C. It also lists the mechanical test method as ASTM A370-2024 and corrosion testing As Per ASTM G28 method 'A'.
What are the required thread specifications?
The certificate demonstrates that Threads are inspected As per ASME B1.13M CL 6g & 6H.