Aluminum 6061-T6 Sample MTC Certificate
Access a comprehensive, professionally formatted Inspection Certificate according to EN 10204-2004 Type 3.1 for Aluminum 6061-T6. Verify high-strength lightweight alloy chemistry and mechanical performance data for aerospace and structural applications.
What's Inside This 6061-T6 MTC Certificate
This sample mill test certificate mirrors the rigorous QA documentation package shipped with every light-alloy order from Ananka Fasteners Pvt. Ltd.
- Full Traceability: Heat and Lot No.: AAXXX linking each hex head cap screw directly back to its original melt.
- Chemical Composition: Detailed verification of Magnesium (0.913%), Silicon (0.625%), and Chromium (0.191%) ensuring structural grade integrity.
- Mechanical Properties: Verified Tensile Strength (335.34 MPa), Yield Strength (307.32 MPa), and Elongation (16.18%) per ASTM E8/E8M:2024.
- Hardness Verification: Recorded results of 87.6 - 88.0 HRB meeting alloy specifications.
- Compliance Verification: Confirmation that the material conforms to ASTM B211 Alloy 6061 T6 EDT. 2012.
- Inspection Data: Confirmed 100% visual inspection and Macro Etch testing per ASTM E-381.
Live Preview: Aluminum 6061-T6 MTC Data
TC Number
QAXXX
TC Date
05.05.202X
Heat Number
HT-AAXXX
Lot Number
AAXXX
Bar Size
10.00 mm
Dimensions / Item
Hex Head Cap Screw M6 x 35mm
Chemical Composition % (Actual Results)
| Magnesium (Mg) | Silicon (Si) | Chromium (Cr) | Copper (Cu) | Manganese (Mn) | Iron (Fe) |
|---|---|---|---|---|---|
| 0.913 | 0.625 | 0.191 | 0.348 | 0.055 | 0.173 |
| 0.80 - 1.20 | 0.40 - 0.80 | 0.04 - 0.35 | 0.15 - 0.40 | Max 0.15 | Max 0.70 |
Mechanical Properties Verification (ASTM E8/E8M:2024)
| Tensile (MPa) | Yield (MPa) | Elongation (%) | Hardness (HRB) |
|---|---|---|---|
| 335.34 | 307.32 | 16.18 | 87.6 - 88.0 |
| Min: 290 | Min: 240 | Min: 9.00 | Verified |
Standard References: lightweight Alloy Compliance
Our Aluminum 6061-T6 certificates confirm compliance with ASTM B211 and ISO standards for mechanical fasteners.
| Standard / Requirement | Confirmation on Certificate |
|---|---|
| ASTM B211 | Material conforms to ASTM B211 Alloy 6061 T6. |
| Visual Inspection | 100% visual inspection carried out & found free from defects. |
| Macro Etch | Macro Etch Test carried out as per ASTM E-381. |
| Radioactive Contamination | Material is certified free from radioactive contamination. |
Ananka Fasteners' Certification Details
Documentation
- EN 10204 Type 3.1
- ISO 9000-2015 Compliant
Mechanicals
- Yield verified > 240 MPa
- Hardness HRB Verified
Inspections
- Macro Etch Verification
- Room Temp (25°C) Testing
Technical FAQs — Aluminum 6061-T6 MTC Certificate
What compliance standards are verified?
The certificate confirms compliance with ASTM B211 Alloy 6061 T6 EDT. 2012 and EN 10204 Type 3.1 standard requirements.
What specific mechanical tests are logged?
The report logs Tensile Strength, Yield Strength, Elongation (%), and Hardness (HRB) according to the ASTM E8/E8M:2024 testing methodology.
Are visual and macro inspections included?
Yes, the certificate validates 100% visual inspection and Macro Etch testing as per ASTM E-381.