Aluminum Bronze C95200 Sample MTC Certificate
Access a comprehensive, professionally formatted Inspection Certificate according to EN 10204-2004: 3.1 for Aluminum Bronze UNS C95200. Verify the exact documentation your QA and engineering teams will receive, featuring heat-traceable chemistry and mechanical verification.
What's Inside This Aluminum Bronze MTC Certificate
This sample mill test certificate mirrors the rigorous documentation package shipped with every high-strength copper alloy order from Ananka Fasteners Pvt. Ltd.
- Full Traceability: Certified with exact Lot No.: LXXX and T.C. No.: S051/25-XXX linked directly back to its original melt.
- Chemical Composition: Detailed verification of Copper (89.24%), Aluminum (9.67%), and Iron (3.43%) ensuring structural alloy integrity.
- Mechanical Properties: Comprehensive reporting of Tensile Strength (504.13 MPa), Yield Strength (234.27 MPa), and Elongation (27.62%).
- Hardness Verification: Recorded results of 122 - 124 BHN meeting specified minimum requirements.
- Standard Compliance: Confirmation that material conforms to ASTM B148 Aluminum Bronze C95200 specifications.
- Quality Inspection: Confirmation of 100% visual inspection and freedom from radioactive contamination.
Material: Aluminum Bronze UNS C95200
Certificate Type: EN 10204-2004 Type 3.1
Form: Hex Bolts 3/8" - 16 UNC
Live Preview: Aluminum Bronze C95200 MTC Data
TC Number
S051/25-XXX
TC Date
23.01.202X
Heat Number
HT-C95XXX
Lot Number
LXXX
Bar Size
12.00 mm
Dimensions / Item
HEX BOLT 3/8" x 50mm
Chemical Composition % (Actual Results)
| Copper (Cu) | Aluminum (Al) | Iron (Fe) |
|---|---|---|
| 89.24 | 9.67 | 3.43 |
| Min: 88.00 | Min: 9.00 | Min: 3.00 |
Mechanical Properties Verification
| Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Hardness (BHN) |
|---|---|---|---|
| 504.13 | 234.27 | 27.62 | 122 - 124 |
| Min: 450.00 | Min: 170.00 | Min: 20.00 | Min: 110 |
Standard References: High-Strength Bronze Compliance
| Standard / Requirement | Confirmation on Certificate |
|---|---|
| ASTM B148 | Material conforms to C95200 EDT. 2024 specifications. |
| Visual Inspection | 100% visual inspection carried out & found free from defects. |
| Weld Repairs | No weld repair performed. |
| Radioactive Contamination | Material is certified free from radioactive contamination. |
Certification Details
Documentation
- EN 10204 3.1 Standard
- ISO 9001:2015 Compliant
Processing
- Hardened at 850°C
- Tempered at 600°C
Finishing
- Surface Finish Applied
- Dimensional Compliance
Technical FAQs
What heat treatment methodology is tracked?
The MTC logs a hardening cycle at 850°C followed by a tempering cycle at 600°C.
What mechanical tests are logged?
Tensile Strength, Yield Strength, Elongation, and Hardness per ASTM A370.
Are visual inspections included?
Yes, 100% visual inspection is confirmed free from defects.