Aluminium 6082 Fasteners – MTC
Aluminium 6082 Sample MTC Certificate
Access a comprehensive, professionally formatted Material Test Certificate according to EN 10204-2004: 3.1 for Aluminium 6082 (ASTM B211 UNS A96082 / EN AW-6082). Inspect the exact documentation your QA and engineering teams will receive with every highly stressed structural fastener order from Ananka Fasteners.
What's Inside This Aluminium 6082 MTC Certificate
This sample mill test certificate mirrors the rigorous QA documentation package standard for our highest-strength 6000-series alloy, perfectly suited for highly stressed applications like trusses, bridges, and transport engineering.
- Full Traceability: Certified with TC No.: S74/26-XX and corresponding European EN AW and ASTM specifications.
- Enhanced Manganese Chemistry: Detailed breakdowns verifying the elevated Silicon (0.70% - 1.30%), Magnesium (0.60% - 1.20%), and Manganese (0.40% - 1.00%) content, which controls the grain structure and provides higher strength than traditional 6061.
- Corrosion Resistance: Explicit verification of trace element controls ensuring the alloy maintains exceptional resistance to industrial and atmospheric corrosion.
- Mechanical Properties (T6 Temper): Comprehensive reporting of Tensile Strength (315.40 MPa), Yield Strength (265.50 MPa), Elongation (11.50%), and Hardness (98 HB), verifying maximum precipitation hardening for heavy structural loads.
- Quality Compliance: 100% visual inspection carried out and verified free from defects and radioactive contamination.
Live Preview: Aluminium 6082 (T6) MTC Data
Review the standard parameters and layout before downloading the full document.
TC Number
S74/26-XX
TC Date
08.07.20XX
Material Spec
ASTM B211 UNS A96082 / EN AW-6082 T6
Bar Shape / Size
Hex Bar / 16 mm
Dimensions / Item
Hex Head Bolt M16 x 75 mm
Quantity
10.00 NOS
Chemical Composition %
| Si | Mg | Mn | Fe | Cr | Zn | Cu | Ti | Al |
|---|---|---|---|---|---|---|---|---|
| 0.95 | 0.85 | 0.65 | 0.32 | 0.15 | 0.08 | 0.05 | 0.04 | Rem |
| 0.70 - 1.30 | 0.60 - 1.20 | 0.40 - 1.00 | Max: 0.50 | Max: 0.25 | Max: 0.20 | Max: 0.10 | Max: 0.10 | Rem |
Mechanical Properties
| TENSILE STRENGTH (Mpa) | YIELD STRENGTH 0.2% Offset (Mpa) | % ELONGATION (GL-50mm) | HARDNESS (HB) |
|---|---|---|---|
| 315.40 | 265.50 | 11.50 | 98 |
| Min: 295 | Min: 250 | Min: 8 | Min: 95 |
Standard References & Compliance
Our MTC certificates map to the demanding industrial standards for fasteners. The test reports confirm compliance with As Per ASME/ASTM B211 UNS A96082 / EN AW-6082 with respect to the tests carried out.
| Standard / Requirement | Confirmation on Certificate |
|---|---|
| Visual Inspection | 100% visual inspection carried out & found free from defects. |
| Safety Requirements | Material is free from radioactive contamination. |
| Weld Repairs | No weld repair Perform. |
| Dimensional Accuracy | All Dimensions are as per PO Specification. |
Certification Details
We confirm that above mentioned Items was Manufactured, Sampled, Tested and Inspected in accordance with the subjected Customer's Purchase Order and as applicable Drawings, Material Specifications, Codes & Standards and the results of the items have been determined to meet the users' requirements.
Documentation Standard
- EN 10204-2004: 3.1 Standard
- Free from radioactive contamination
- Certified ISO 9001: 2015 Company
Heat Treatments
- Solution Heat Treated & Artificially Aged (T6 Temper)
- Highest Strength of the 6000 Series
Testing Conditions
- Chemical, Mechanical & hardness test carried at room temperature 25°C
- 100% visual inspection carried out
Technical FAQs — Aluminium 6082 MTC Certificate
How does Aluminium 6082 differ from Aluminium 6061?
Aluminium 6082 is often considered the European equivalent to 6061, but it features a higher Manganese content (0.40% - 1.00%). This addition of Manganese controls the grain structure, allowing 6082 to achieve slightly higher tensile and yield strength than 6061, making it the highest strength alloy in the 6000 series.
What are the typical applications for 6082 fasteners?
Due to its excellent strength-to-weight ratio and superior corrosion resistance, Aluminium 6082 in the T6 temper is heavily utilized in highly stressed applications. This includes structural trusses, scaffolding, bridges, heavy transport vehicles, and offshore engineering.
Are the materials free from radioactive contamination?
Yes, the document strictly states that the material is free from radioactive contamination and undergoes a 100% visual inspection to ensure it is free from defects.