ASTM A182 GRADE F9
ASTM A182 Grade F9 Sample MTC Certificate
Access a comprehensive, professionally formatted Material Test Certificate according to EN 10204-2004: 3.1 for ASTM A182 Grade F9 (UNS S50400). Inspect the exact documentation your QA and engineering teams will receive with every high-temperature, highly corrosive-resistant forged steel order.
What's Inside This Grade F9 MTC Certificate
This sample mill test certificate mirrors the rigorous QA documentation package standard for highly alloyed, high-temperature forged components shipped from our facilities.
- Full Traceability: Certified with TC No.: F9/26-XX and corresponding ASTM A182 specifications.
- High-Temperature Chemistry: Detailed breakdowns verifying the powerful 9% Chromium (8.00–10.00%) and 1% Molybdenum (0.90–1.10%) composition, providing vastly superior oxidation resistance and high-temperature strength compared to lower F-grades.
- Verified Heat Treatment: Explicit documentation of the Normalized and Tempered process, ensuring the material meets the structural and toughness requirements for critical pressure vessels and refinery systems.
- Mechanical Properties: Comprehensive reporting of Tensile Strength (615.50 MPa), Yield Strength (410.20 MPa), Elongation (25.50%), and Hardness (195, 198, 192 HBW) per ASTM A182 requirements.
- Quality Compliance: 100% visual inspection carried out and verified free from defects and radioactive contamination.
Live Preview: ASTM A182 Grade F9 MTC Data
Review the standard parameters and layout before downloading the full document.
TC Number
F9/26-XX
TC Date
18.11.20XX
Material Spec
ASTM A182 Grade F9 (UNS S50400)-2023
Bar Shape / Size
Forged Round Bar / 75 mm
Dimensions / Item
Forged Round Bar 75mm Dia x 1000mm
Quantity
30.00 NOS
Chemical Composition %
| C | Mn | P | S | Si | Cr | Mo | Fe |
|---|---|---|---|---|---|---|---|
| 0.12 | 0.45 | 0.015 | 0.010 | 0.75 | 9.25 | 1.02 | Rem |
| Max: 0.15 | Min: 0.30 Max: 0.60 |
Max: 0.030 | Max: 0.030 | Min: 0.50 Max: 1.00 |
Min: 8.00 Max: 10.00 |
Min: 0.90 Max: 1.10 |
Rem |
Mechanical Properties
| TENSILE STRENGTH (MPa) | YIELD STRENGTH 0.2% Offset (MPa) | % ELONGATION (GL-50mm) | HARDNESS (HBW) |
|---|---|---|---|
| 615.50 | 410.20 | 25.50 | 195, 198, 192 |
| Min: 585 | Min: 380 | Min: 20 | Max: 250 |
Standard References & Compliance
Our MTC certificates map to the demanding industrial standards for high-temperature pressure piping components. The test reports confirm compliance with As Per ASME/ASTM A182 Grade F9 EDT. 2023 with respect to the tests carried out.
| Standard / Requirement | Confirmation on Certificate |
|---|---|
| Visual Inspection | 100% visual inspection carried out & found free from defects. |
| Safety Requirements | Material is free from radioactive contamination. |
| Weld Repairs | No weld repair Perform. |
| Dimensional Accuracy | All Dimensions are as per PO Specification. |
Certification Details
We confirm that above mentioned Items was Manufactured, Sampled, Tested and Inspected in accordance with the subjected Customer's Purchase Order and as applicable Drawings, Material Specifications, Codes & Standards and the results of the items have been determined to meet the users' requirements.
Documentation Standard
- EN 10204-2004: 3.1 Standard
- Free from radioactive contamination
- Certified ISO 9001: 2015 Company
Heat Treatments
- Normalized and Tempered
- Min. Tempering Temp: 675°C (1250°F)
Testing Conditions
- Chemical, Mechanical & hardness test carried at room temperature 25°C
- 100% visual inspection carried out
Technical FAQs — ASTM A182 Grade F9 MTC
What is the significance of the 9% Chromium and 1% Molybdenum in Grade F9?
The 9% Chromium content provides Grade F9 with substantial resistance to oxidation and high-temperature corrosion, significantly outperforming lower grades like F11 or F22. The 1% Molybdenum specifically enhances the alloy's high-temperature creep strength, making it ideal for the extreme thermal environments found in modern refineries and power generation plants.
What heat treatment is documented on this MTC?
ASTM A182 F9 forgings are required to be Normalized and Tempered (or Quenched and Tempered). This MTC confirms the specific process applied, including a mandatory tempering cycle at a minimum of 675°C (1250°F). This stabilizes the high-alloy microstructure and provides the necessary toughness and ductility.
What are the primary applications for F9 forgings?
Grade F9 is extensively utilized in the petrochemical industry, oil refineries, and power generation facilities. It is the material of choice for forged flanges, high-pressure valves, and piping fittings that are exposed to severe, high-temperature corrosive environments, typically operating safely up to 600°C (1112°F).