Inconel 625 Sample MTC Certificate
Access a comprehensive, professionally formatted Material Test Certificate according to EN 10204-2004: 3.1 for Inconel 625 (UNS N06625). Verify the exact documentation your QA and engineering teams will receive, featuring heat-traceable chemistry and solution annealing records.
What's Inside This Inconel 625 MTC Certificate
This sample mill test certificate mirrors the documentation package shipped with every high-performance Nickel-Chromium alloy order from Ananka Fasteners Pvt. Ltd.
- Full Traceability: Certified with exact Lot No.: HXXX and TC No.: S07/26-XXX linked back to its original melt.
- Chemical Composition: Detailed verification of Nickel (60.28%), Chromium (21.970%), and Molybdenum (9.460%) per ASTM B446.
- Heat Treatment Data: Records for Solution Annealing at 900°C for 2 Hours followed by a Water Quench.
- Mechanical Properties: Comprehensive reporting of Tensile Strength (904.00 MPa), Yield Strength (450.00 MPa), and Hardness (25-26 HRC).
- Quality Inspection: Confirmation of 100% visual inspection and freedom from radioactive contamination.
- Standard Compliance: Verified conformance to UNS N06625 ED-2024 specifications.
Material: Inconel 625 (UNS N06625)
Certificate Type: EN 10204-2004 Type 3.1
Form: Dowel Pins 9mm Dia
Live Preview: Inconel 625 MTC Data
TC Number
S0X/2X-2X
TC Date
0X.0X.202X
Heat Number
HT-625XXX
Lot Number
HXXX
Bar Size
9.00 mm
Dimensions / Item
Dowel Pins 9mm x 25mm
Chemical Composition % (Actual Results)
| Nickel (Ni) | Chromium (Cr) | Molybdenum (Mo) | Nb + Ta | Iron (Fe) | Carbon (C) |
|---|---|---|---|---|---|
| 60.28 | 21.970 | 9.460 | 3.920 | 3.650 | 0.070 |
| Min: 58.00 | 20.00 - 23.00 | 8.00 - 10.00 | 3.150 - 4.150 | Max: 5.00 | Max: 0.100 |
Mechanical Properties Verification
| Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Hardness (HRC) |
|---|---|---|---|
| 904.00 | 450.00 | 51.10 | 25, 26, 25 |
| Min: 828 | Min: 414 | Min: 30 | Verified |
Standard References: High-Temperature Alloy Compliance
Our Inconel 625 certificates confirm compliance with ASTM B446 and EN standards for corrosion-resistant Nickel alloys.
| Standard / Requirement | Confirmation on Certificate |
|---|---|
| ASTM B446 | Material conforms to UNS N06625 ED-2024 specifications. |
| Visual Inspection | 100% visual inspection carried out & found free from defects. |
| Heat Treatment | Solution Annealing recorded at 900°C with Water Quench. |
| Contamination | Material is certified free from radioactive contamination. |
Ananka Fasteners' Certification Details
Documentation
- EN 10204 3.1 Standard
- ISO 9001:2015 Compliant
- Full Heat/Lot Traceability
Heat Treatments
- Solution Annealed at 900°C
- Soak Time: 2 Hours
- Verified Water Quench
Testing Conditions
- Yield Strength > 414 MPa
- Radioactive Contamination Free
- Dimensional Compliance
Technical FAQs — Inconel 625 MTC Certificate
What heat treatment methodology is tracked?
The MTC specifically logs a Solution Annealing process at 900°C for 2 Hours followed by a Water Quench, crucial for achieving proper grain structure and corrosion resistance.
What specific tests are logged?
The report includes complete chemical analysis (verifying high Nickel and Chromium content), mechanical testing (Tensile, Yield, Elongation), and Hardness testing (HRC) per ASTM B446 specifications.
Are dimensional and visual checks included?
Yes, the certificate confirms 100% visual inspection found free from defects and dimensional conformance for the 9mm Dowel Pins.