Super Duplex S32760 Sample MTC Certificate
Access a comprehensive, professionally formatted Material Test Certificate according to EN 10204-2004: 3.1 for Super Duplex Stainless Steel S32760. Verify the exact documentation your QA and engineering teams will receive, featuring PREN verification, corrosion testing, and high-strength mechanical data.
What's Inside This Super Duplex MTC Certificate
This sample mill test certificate mirrors the rigorous QA documentation package shipped with every Super Duplex S32760 order from Ananka Fasteners Pvt Ltd.
- Full Traceability: Certified with Heat No. N27XXX and Lot No.: RXXX linked directly back to its original melt.
- Chemical Composition & PREN: Detailed breakdown of Cr, Ni, Mo, N, and W with a verified PREN value of 43.100.
- Mechanical Properties: Comprehensive reporting of Tensile Strength (849.31 MPa), Yield Strength (690.83 MPa), and Impact testing at -101°C.
- Corrosion Testing: Verified G48 Method 'A' pitting corrosion test at 50°C and Ferrite test per ASTM E562.
- Compliance Verification: Confirmation that material fulfills NACE MR0175/ISO 15156 and ASTM A1082 requirements.
Material: ASTM A1082 S32760 EDT. 2024
Certificate Type: EN 10204-2004 Type 3.1
Form: 1/2" Stud Bolt
Live Preview: Super Duplex S32760 MTC Data
TC Number
S11/26-XXX
TC Date
11.04.202X
Heat Number
N27XXX
Lot Number
RXXX
PREN Value
43.100
Dimensions
1/2" Stud Bolt x 100mm
Chemical Composition % (Actual Results)
| Cr | Ni | Mo | N | W | Cu | C |
|---|---|---|---|---|---|---|
| 25.400 | 6.740 | 3.800 | 0.254 | 0.666 | 0.561 | 0.024 |
| 24.0-26.0 | 6.0-8.0 | 3.0-4.0 | 0.2-0.3 | 0.5-1.0 | 0.5-1.0 | Max 0.03 |
Mechanical Properties (Test Method: ASTM A370)
| Tensile (MPa) | Yield (MPa) | Elongation (%) | Impact Avg (J) | Hardness (HRC) |
|---|---|---|---|---|
| 849.31 | 690.83 | 40.86 | 97.33 | 27.4 - 28.6 |
| Min: 750 | Min: 550 | Min: 25 | Min: 35 | Max: 30 |
Standard References: Super Duplex Compliance
Our Super Duplex S32760 MTC certificates confirm compliance with the most stringent oil, gas, and marine specifications including NACE and ISO standards.
| Standard / Requirement | Confirmation on Certificate |
|---|---|
| ASTM G48 Method A | Pitting corrosion test at 50°C for 24 hours - No pitting observed. |
| ASTM E562 | Ferrite test performed and found satisfactory. |
| NACE MR0175 | Verified compliance for use in H2S-containing environments. |
| ASTM A923 Method A | Metallographic Examination at 400X magnification. |
Ananka Fasteners' Certification Details
Documentation
- EN 10204 3.1 Standard
- ISO 9000-2015 Compliant
Corrosion Testing
- G48 Pitting Verification
- Ferrite Phase Balance
Mechanicals
- Charpy Impact at -101°C
- PREN > 40 Guaranteed
Technical FAQs — Super Duplex S32760 MTC Certificate
What corrosion testing is tracked on this certificate?
The MTC logs ASTM G48 Method A pitting corrosion testing at 50°C for 24 hours, ensuring the material can withstand harsh marine and chemical environments without pitting.
What specific mechanical tests are logged?
The report includes Tensile Strength, Yield Strength, and specialized Impact Testing at -101°C, along with Hardness testing (HRC) to meet NACE MR0175 compliance.
Are microstructural examinations included?
Yes, the certificate validates Ferrite content per ASTM E562 and includes Metallographic Examination at 400X magnification as per ASTM A923 Method A.